| 优异力学性能 ，高流动， 优异的刚韧平衡， 易加工成型 |
| Product Description | |
|---|---|
| Supplier | Polysyron |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,High liquidity,Rigid-tough balance |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Shrinkage rate | 0.4-0.7 | % | ISO 294-4 |
| Density | 1.15 | g/cm³ | ISO 1183-1 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 18 | g/10min | ISO 1133 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa | 120 | ℃ | ISO 75-2 |
| Flame retardant level | |||
| 1.60 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| bending strength | 70 | MPa | ISO 178 |
| Tensile strain | 80 | % | ISO 527 |
| tensile strength | 50 | MPa | ISO527 |
| Rockwell hardness | 108 | R 级 | ISO 2039-2 |
| Bending modulus | 2200 | MPa | ISO178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod notched impact strength | |||
| 23℃ | 48 | kJ/m² | ISO 179-1:2001 |
| Process Conditions | |||
|---|---|---|---|
| Typical processing conditions | Nominal value | Unit | Test method |
| Melt temperature | 230-250 | ℃ | |
| Temperature of the front section of the material barrel | 250-285 | ℃ | |
| Temperature in the middle section of the barrel | 245-275 | ℃ | |
| Temperature of the rear section of the barrel | 240-265 | ℃ | |
| Injection molding speed | 中高速 | ||
| Dry conditions | 90~110℃，3~6h | ||
| Mold temperature | 60~100 | ℃ | |
| Back pressure | 0.3~1.0 | Mpa | |
| Processing upper limit temperature | 290 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |