| About |
|---|
| Pearlbond™ DIPP-119 is polycaprolactone copolyester based thermoplastic polyurethane, supplied in form of translucent pellets. Featuring low melting point and excellent transparency, this product offers excellent flexibility, elasticity and easy processing. Ideally used for extrusion or compounding with PVC. APPLICATIONS Pearlbond™ DIPP-119 is used mostly in extrusion applications where low melting point as well as improved adhesion over polar substrates is highly appreciated. It is ideal for PVC compounding. It is also used in solvent coatings on textile substrates.&& |
| Product Description | |
|---|---|
| Supplier | Lubrizol Advanced Materials |
| Generic | TPU-Capro |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Clarity,Good flexibility,High elastic,Aromatic |
| Availabilitys | North America,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.16 | g/cm³ | ASTM D792 |
| 20℃ | 1.16 | g/cm³ | ISO 2781 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 25 to 50 | g/10min | ISO 1133 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| fracture | 12.0 | MPa | ASTM D412 |
| 100% strain | 2.00 | MPa | ASTM D412 |
| 300% strain | 3.00 | MPa | ASTM D412 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 100 to 110 | ℃ | Internal Method |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Softening range | 90 to 100 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 70 | ASTM D2240 , ISO 868 | |
| tensile strength | ISO 527-2 | ||
| — | 12.0 | MPa | ISO 527-2 |
| 100% strain | 2.00 | MPa | ISO 527-2 |
| 300% strain | 3.00 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 800 | % | ASTM D412 |
| fracture | 800 | % | ISO 527-2 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 70 to 80 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Barrel 1 zone temperature | 120 to 130 | °C | |
| Barrel 2 zone temperature | 145 to 155 | °C | |
| Barrel 3 zone temperature | 160 to 170 | °C | |
| Barrel 4 zone temperature | 165 to 175 | °C | |
| Nozzle temperature | 145 to 155 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 20°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |