| About |
|---|
| PEARLTHANE® 11T85UV is a UV resistant polycaprolactone copolyester based TPU, supplied in form of translucent, colourless pellets, featuring adequate hardness with excellent flow and mechanical properties. It can be injection-molded and coextruded. PEARLTHANE® 11T85UV when processed by injection moulding, can be used for making automotive parts and a variety of technical components. PEARLTHANE® 11T85UV when processed by coextrusion, can be used for making technical sheets thanks to its excellent adhesion into polar substrates such as ABS, PC and PVC.&& |
| Product Description | |
|---|---|
| Supplier | Lubrizol Advanced Materials |
| Generic | TPU-Capro |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High liquidity,Good bond |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.16 | g/cm³ | ASTM D792 |
| 20℃ | 1.16 | g/cm³ | ISO 2781 |
| water content | < 0.10 | % | Internal Method |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 , ISO 527 | ||
| yield | 40.0 | MPa | ASTM D412 , ISO 527 |
| 100% strain | 6.00 | MPa | ASTM D412 , ISO 527 |
| 300% strain | 10.0 | MPa | ASTM D412 , ISO 527 |
| Tensile strain | |||
| fracture | 630 | % | ASTM D412，ISO 527 |
| tear strength | |||
| — | 90.0 | kN/m | ASTM D624 |
| — | 90 | kN/m | ISO 34-1 |
| Compression deformation | ASTM D395B | ||
| 23℃，70 hr | 20 | % | ASTM D395B |
| 70℃，22 hr | 35 | % | ASTM D395B |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -40.0 | ℃ | ISO 11357-2 |
| Melting temperature | 178 to 188 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 86 | ASTM D2240 , ISO 868 | |
| Wear amount | 25.0 | mm³ | ISO 4649 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 100 to 110 | °C | |
| Drying time | 1.0 to 2.0 | hr | |
| Barrel rear temperature | 195 | °C | |
| Barrel middle temperature | 200 | °C | |
| Barrel front temperature | 210 | °C | |
| Nozzle temperature | 210 | °C | |
| Mold temperature | 35 | °C | |
| Drying temperature | 100 to 110 | °C | |
| Drying time | 1.0 to 2.0 | hr | |
| Barrel 1 zone temperature | 175 to 195 | °C | |
| Barrel 2 zone temperature | 185 to 205 | °C | |
| Barrel 3 zone temperature | 195 to 215 | °C | |
| Barrel 4 zone temperature | 200 to 220 | °C | |
| Nozzle temperature | 190 to 210 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 3. 10°C /min |
| 4. Temperature at which MFI = 10 g/10 min @ 21.6 kg |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |