Pearlthane® 11T92EM

About
Pearlthane® 11T92EM is a polycaprolactone copolyester based TPU, supplied in form of translucent, colourless pellets, combining hardness with excellent mechanical properties. It can be extruded and injection-moulded. Pearlthane® 11T92EM can be extruded into profiles, belts, tubes and film. In the case of injection moulding, this grade is only recommended for certain specific applications, e.g. when large, hard-to-fill mould cavities are used.&&

About

Pearlthane® 11T92EM is a polycaprolactone copolyester based TPU, supplied in form of translucent, colourless pellets, combining hardness with excellent mechanical properties. It can be extruded and injection-moulded. Pearlthane® 11T92EM can be extruded into profiles, belts, tubes and film. In the case of injection moulding, this grade is only recommended for certain specific applications, e.g. when large, hard-to-fill mould cavities are used.&&

Product Description
Supplier	Lubrizol Advanced Materials
Generic	TPU-Capro
Material Status	Commercial: Active
Availabilitys	North America,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density
—	1.16	g/cm³	ASTM D792
20℃	1.16	g/cm³	ISO 2781
water content	< 0.10	%	Internal Method

elastic body	Nominal value	Unit	Test method
tensile strength			ASTM D412 , ISO 527
yield	35.0	MPa	ASTM D412 , ISO 527
100% strain	8.00	MPa	ASTM D412 , ISO 527
300% strain	12.0	MPa	ASTM D412 , ISO 527
Tensile strain
fracture	600	%	ASTM D412，ISO 527
tear strength
—	100	kN/m	ASTM D624
—	100	kN/m	ISO 34-1
Compression deformation			ASTM D395B
23℃，70 hr	25	%	ASTM D395B
70℃，22 hr	43	%	ASTM D395B

THERMAL	Nominal value	Unit	Test method
Glass transition temperature	-38.0	℃	ISO 11357-2
Melting temperature	180 to 190	℃	Internal Method

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s A	91		ASTM D2240 , ISO 868
Wear amount	25.0	mm³	ISO 4649

Process Conditions
injection	Nominal value	Unit	Test method
Extrusion	Nominal value	Unit	Test method
Drying temperature	100 to 110	°C
Drying time	1.0 to 2.0	hr
Barrel rear temperature	195	°C
Barrel middle temperature	200	°C
Barrel front temperature	210	°C
Nozzle temperature	210	°C
Mold temperature	35	°C
Drying temperature	100 to 110	°C
Drying time	1.0 to 2.0	hr
Barrel 1 zone temperature	190 to 200	°C
Barrel 2 zone temperature	195 to 210	°C
Barrel 3 zone temperature	200 to 215	°C
Barrel 4 zone temperature	200 to 220	°C
Nozzle temperature	190 to 210	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.