| Product Description | |
|---|---|
| Supplier | Arkema |
| Material Status | Commercial: Active |
| Features | Weather resistance is good |
| Availabilitys | Asia Pacific,Europe,North America,Latin America,Africa & Middle East |
| Process Methods | Extrusion,Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.01 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD：4.0 mm，24 hrs | 1.4 | % | ISO 294-4 |
| MD：4.0 mm，24 hrs | 1.2 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.70 | % | ISO 62 |
| 23℃，24hr | 1.1 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shaw’s D | 58 | ISO 868 | |
| tensile strength | |||
| Yield, drying | 19 | MPa | ISO 527-2 |
| Yield, moisten | 18 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | >50 | % | ISO 527-2 |
| yield | 22 | % | ISO 527-2 |
| Bending modulus | 285 | MPa | ISO 178 |
| Tensile modulus | |||
| desiccation | 307 | MPa | ISO 527-2 |
| moist | 285 | MPa | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30 ℃, completely fractured | 20 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 85 | ℃ | ISO 306 |
| Melting temperature | 169 | ℃ | ISO 11357-3 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| extrusion | Nominal value | Unit | Test method |
| drying temperature | 65 to 75 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Processing (melt) temperature | 230 to 290 | °C | |
| Mold temperature | 25 to 60 | °C | |
| drying temperature | 65 to 75 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Melt Temperature | 210 to 240 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |