| About |
|---|
| PEEK-OPTIMA® polymer from Invibio® is a high performance biomaterial providing advanced solutions for implant manufacturers. Formulated to meet the most exacting in-vivo criteria, PEEK-OPTIMA is biocompatible, safe and stable.&& |
| Product Description | |
|---|---|
| Generic | PEEK |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good disinfection,Steam sterilized,Hydrolysis stability,Biocompatible,Radiation disinfection,Good wear resistance,Solvent resistance,Ethylene oxide disinfection |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.29 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.0 mm | 1.2 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.50 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 63 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | 无断裂 | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 340 | ℃ | DSC |
| Linear coefficient of thermal expansion | |||
| MD | ASTM D696 | ||
| — | 4.7E-5 | cm/cm/℃ | ASTM D696 |
| — | 1.1E-4 | cm/cm/℃ | ASTM D696 |
| Relative temperature index | 260 | ℃ | UL 746 |
| Electrical performance | 260 | ℃ | UL 746 |
| Impact mechanical performance | 260 | ℃ | UL 746 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 99 | ASTM D785 | |
| tensile strength | |||
| yield | 100 | MPa | ISO 527-2/1B/50 |
| Tensile strain | |||
| fracture | 20 | % | ISO 527-2/1B/50 |
| Bending modulus | 4000 | MPa | ISO 178 |
| bending strength | 170 | MPa | ISO 178 |
| compressive strength | 118 | MPa | ASTM D695 |
| shear modulus | 1300 | MPa | ASTM D732 |
| shear strength | 53.1 | MPa | ASTM D732 |
| Poisson’s ratio | 0.40 | ASTM E132 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 150 | °C | |
| Drying time | 3.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Proposed maximum recycled material ratio | 0 | % | |
| Barrel rear temperature | 350 to 355 | °C | |
| Barrel middle temperature | 355 to 365 | °C | |
| Barrel front temperature | 360 to 370 | °C | |
| Nozzle temperature | 365 to 375 | °C | |
| Mold temperature | 160 to 200 | °C | |
| Injection pressure | 7.00 to 14.0 | MPa | |
| Hold pressure | 4.00 to 10.0 | MPa | |
| Back pressure | 0.200 to 5.00 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Clamping force | 5.0 to 8.0 | kN/cm² | |
| Screw length to diameter ratio | 18.0:1.0 to 24.0:1.0 | ||
| Screw compression ratio | 2.0 : 1.0 to 3.0 : 1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Below Tg |
| 3. Above Tg |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |