| About |
|---|
| PELPRENE™ P150B-05 is a Thermoplastic Polyester Elastomer (TPEE) product. It is available in North America. Typical application: Automotive. Characteristics include: Flame Rated Low to No Odor/Taste&& |
| Product Description | |
|---|---|
| Supplier | TOYOBO |
| Generic | TPEE |
| Material Status | Commercial: Active |
| Features | Low odor,HB |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.23 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 20 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：2.0 mm | 1.3 | % | ASTM D955 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 65% RH | 0.36 | % | ASTM D570 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 176 | kN/m | ASTM D624 |
| Compression deformation | 60 | % | JIS K6301 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 无断裂 | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 117 | ℃ | ASTM D648 |
| Embrittlement temperature | < -65.0 | ℃ | JIS K6301 |
| Vicat Softening Temp | 190 | ℃ | ASTM D1525 |
| Melting temperature | 212 | ℃ | DSC |
| Linear coefficient of thermal expansion | |||
| MD | 1.4E-4 | 1/℃ | ASTM E831 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 2.0E+14 | ohms·cm | ASTM D257 |
| Dielectric strength | 30 | kV/mm | JIS K2111 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Resilience | 59.0 | JIS K6301 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 98 | JIS K6301 | |
| Shaw’s D | 57 | ASTM D2240 | |
| tensile strength | ASTM D638 | ||
| — | 38.0 | MPa | ASTM D638 |
| 50% strain | 19.6 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 500 | % | ASTM D638 |
| Bending modulus | 289 | MPa | ASTM D790 |
| compressive strength | |||
| 10% strain | 19.1 | MPa | ASTM D695 |
| Taber abraser | |||
| 1000 cycles | 10.0 | mg | ASTM D1044 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |