| About |
|---|
| Low viscosity, heat stabilised polyamide 6, 10% glass fiber and 20% glass bead reinforced&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Low Viscosity,Heat Stabilized,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.35 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.70 | % | ISO 294-4 |
| MD | 0.55 | % | ISO 294-4 |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 6.5 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 2.1 | % | ISO 62 |
| Viscosity number | 125 | cm³/g | ISO 307 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 5500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 100 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 2.9 | % | ISO 527-2/5 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 45 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 205 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 185 | ℃ | ISO 75-2/A |
| Melting temperature | 222 | ℃ | ISO 11357-3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | PA6, MHRC, 12-060 N, GF10+GB20 | ISO 1874 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 3.0 | hr | |
| Recommended maximum moisture content | 0.050 to 0.13 | % | |
| Proposed maximum recycled material ratio | 20 | % | |
| Barrel rear temperature | 260 to 280 | °C | |
| Barrel middle temperature | 265 to 290 | °C | |
| Barrel front temperature | 270 to 280 | °C | |
| Processing (melt) temperature | 255 to 295 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Injection pressure | 71.5 | MPa | |
| Screw length to diameter ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw compression ratio | 2.2:1.0 to 2.8:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |