| About |
|---|
| Petra 130 FR is a 30% glass fiber reinforced, flame retardant injection molding compound based on post-consumer and post-industrial recycle polyethylene terephthalate feedstocks. It is recognized as UL 94V-0/5VA by Underwriters Laboratories. It is also available in pigmented versions. Applications Petra 130 FR is generally recommended for applications such as electrical housing and bobbins.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PET |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,HB |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.55 | g/cm³ | ASTM D792, ISO 1183 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 9.0 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 95 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 240 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 220 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 210 | ℃ | ISO 75-2/A |
| Melting peak temperature | 245 | ℃ | ASTM D3418, ISO 3146 |
| Linear coefficient of thermal expansion | |||
| MD | 2.3E-5 | 1/℃ | ASTM E831 |
| Relative temperature index | UL 746 | ||
| Electrical performance | UL 746 | ||
| 0.750 mm | 140 | ℃ | |
| Impact mechanical performance | UL 746 | ||
| 1.50 mm | 140 | ℃ | |
| 0.75 mm | 140 | ℃ | |
| 3.00 mm | 140 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 1.50 mm | > 1.0E+13 | ohms·cm | ASTM D257 |
| — | > 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1.5 mm | 22 | kV/mm | ASTM D149 |
| — | 40 | kV/mm | IEC 60243-1 |
| Dielectric constant | IEC 60250 | ||
| 100 Hz | 3.70 | ||
| 1 MHz | 3.50 | ||
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 0.020 | ||
| 1 MHz | 0.020 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.3mm | V-0 | UL 94 | |
| 0.75mm | V-0/5VA | UL 94 | |
| 1.5mm | V-0/5VA | UL 94 | |
| 3.0mm | V-0/5VA | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 118 | ASTM D785 | |
| Tensile modulus | ISO 527-2 | ||
| -40℃ | 10400 | MPa | |
| 23℃ | 10200 | MPa | |
| 80℃ | 4950 | MPa | |
| 121℃ | 2940 | MPa | |
| tensile strength | ASTM D638, ISO 527-2 | ||
| Fracture, -40 ℃ | 210 | MPa | |
| Fracture, 23 ℃ | 155 | MPa | |
| Fracture, 80 ℃ | 80.0 | MPa | |
| Fracture, 121 ℃ | 65.0 | MPa | |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ASTM D638 |
| Fracture, 23 ℃ | 3.5 | % | ISO 527-2 |
| Bending modulus | ASTM D790 | ||
| -40℃ | 9660 | MPa | |
| 23℃ | 8970 | MPa | |
| 65℃ | 6130 | MPa | |
| 90℃ | 3440 | MPa | |
| 121℃ | 2830 | MPa | |
| bending strength | ASTM D790 | ||
| -40℃ | 275 | MPa | |
| 23℃ | 240 | MPa | |
| 65℃ | 170 | MPa | |
| 90℃ | 105 | MPa | |
| 121℃ | 85.0 | MPa |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 120 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 100 to 110 | °C | |
| Injection pressure | 3.50 to 12.5 | MPa | |
| Injection speed | 快速 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method A (Short-Time) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |