| F0554 is a high molecular weight high density polyethylene resin designed for blown film applications. This resin has broad molecular weight distribution that makes it easier to process. Films made from this resin exhibit high stiffness, excellent impact and toughness characteristics. Applications Shopping bag Trash bag Industrial liner&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good flexibility,High impact resistance,Wide molecular weight distribution,High molecular weight |
| Availabilitys | Africa & Middle East |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.951 | g/cm³ | ASTM D792-A |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 0.050 | g/10min | ASTM D1238 |
| 190℃，21.6kg | 9.3 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 20 | µm | |
| Secant modulus | ASTM D882 | ||
| 1% secant, MD: 20 µ m | 930 | MPa | ASTM D882 |
| 1% secant, MD: 20 µ m | 990 | MPa | ASTM D882 |
| 1% secant, TD: 20 µ m | 1030 | MPa | ASTM D882 |
| 1% secant, TD: 20 µ m | 1140 | MPa | ASTM D882 |
| tensile strength | |||
| MD, yield, 20 µ m | 35.0 | MPa | ASTM D882 |
| TD, yield, 20 µ m | 30.0 | MPa | ASTM D882 |
| MD, fracture, 20 µ m | 70.0 | MPa | ASTM D882 |
| MD, fracture, 20 µ m | 75.0 | MPa | ASTM D882 |
| TD, fracture, 20 µ m | 65.0 | MPa | ASTM D882 |
| TD, fracture, 20 µ m | 55.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 20 µ m | 560 | % | ASTM D882 |
| MD, fracture, 20 µ m | 520 | % | ASTM D882 |
| TD, fracture, 20 µ m | 550 | % | ASTM D882 |
| TD, fracture, 20 µ m | 560 | % | ASTM D882 |
| Drop hammer impact | ASTM D1709 | ||
| 20 µm | 330 | g | ASTM D1709 |
| 20 µm | 250 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：20 µm | 17 | g | ASTM D1922 |
| MD：20 µm | 11 | g | ASTM D1922 |
| TD：20 µm | 39 | g | ASTM D1922 |
| TD：20 µm | 78 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 126 | ℃ | ASTM D1525 4 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 180 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. With Stabilizer |
| 3. Without Stabilizer |
| 4. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |