| FS253S is a linear low density polyethylene resin designed for blown film applications. This resin has a relatively high MFR that makes it an easy processing material. Films made from this resin exhibits high transparency, good toughness and good extrusion characteristics. Applications General purpose film Garment packaging Agriculture film&& |
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Clarity,Good flexibility |
| Availabilitys | Africa & Middle East |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.921 | g/cm³ | ASTM D792-A |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.2 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | ASTM D1894 | ||
| With oneself – dynamic | 0.080 | ASTM D1894 | |
| With oneself – static | 0.11 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 30 | µm | |
| Secant modulus | ASTM D882 | ||
| 1% secant, MD: 30 µ m | 205 | MPa | ASTM D882 |
| 1% secant, TD: 30 µ m | 250 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, fracture, 30 µ m | 35.0 | MPa | ASTM D882 |
| TD, fracture, 30 µ m | 30.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 30 µ m | 770 | % | ASTM D882 |
| TD, fracture, 30 µ m | 930 | % | ASTM D882 |
| Drop hammer impact | |||
| 30 µm | 90 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：30 µm | 130 | g | ASTM D1922 |
| TD：30 µm | 350 | g | ASTM D1922 |
| Adhesive load | 14 | g | ASTM D3354 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 122 | ℃ | DSC |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45°，30 µm | 55 | ASTM D2457 | |
| Haze | |||
| 30 µm | 15 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 160 to 200 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |