| About |
|---|
| M8060 is a high density polyethylene resin intended for injection molding. This resin has good flow characteristics that make it easier to process. Injection molding parts made from this resin exhibits high modulus and low warpage. Applications Transport and storage containers Cartridges Technical parts with moderate ESCR requirements Closures for still mineral waters&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Low warping,Good liquidity |
| Availabilitys | Africa & Middle East |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.960 | g/cm³ | ASTM D792-A |
| Melt Flow Rate | |||
| 190℃，2.16kg | 8.0 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 10% non-ionic detergent, F50 | 5.00 | hr | ASTM D1693 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 3.0 | kJ/m² | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 127 | ℃ | ASTM D1525 2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 68 | ASTM D2240 | |
| tensile strength | ASTM D638 | ||
| yield | 29.0 | MPa | ASTM D638 |
| fracture | 16.0 | MPa | ASTM D638 |
| Bending modulus | 1430 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 160 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |