| About |
|---|
| Petrothene NA143063 is a homopolymer resin selected by customers for blown film. Typical applications include stiff liners. NA143063 exhibits good processability and clarity.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Food contact compliance,Homopolymer |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 32 | µm | |
| Secant modulus | |||
| 1% 正割，TD，32 µm，吹塑薄膜 | 221 | MPa | ASTM E111 |
| 1% secant, MD, 32 µ m, blow molded film | 193 | MPa | ASTM E111 |
| tensile strength | |||
| Yield, 1.91 mm | 11.9 | MPa | ASTM D638 |
| TD, yield, 32 µ m, blow molded film | 17.2 | MPa | ASTM D882 |
| MD, yield, 32 µ m, blow molded film | 23.4 | MPa | ASTM D882 |
| Tensile strain | |||
| fracture | 650 | % | ASTM D638 |
| TD, fracture, 32 µ m, blow molded film | 500 | % | ASTM D882 |
| MD, fracture, 32 µ m, blow molded film | 300 | % | ASTM D882 |
| Drop hammer impact | |||
| 32 µ m, blow molded film | 90 | g | ASTM D1709 |
| tear strength | |||
| TD, 32 µ m, blow molded film | 200 | g | ASTM D1922 |
| MD, 32 µ m, blow molded film | 380 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 93.0 | ℃ | ASTM D1525 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 31.8 µ m, blow molded film | 70 | ASTM D2457 | |
| Haze | |||
| 31.8 µ m, blow molded film | 6.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |