| About |
|---|
| Sylvin 8839-60D White 1403 Is Semi-rigid Vinyl Compound Formulated For Exterior Extruded Cap Stock Applications That Require Higher Gloss.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Good surface appearance |
| Availabilitys | North America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.926 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.50 | g/10min | ASTM D1238 |
| Vinyl acetate content | 6.6 | wt% | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 51 | µm | |
| Secant modulus | |||
| 1% secant, TD, 51 µ m, blow molded film | 145 | MPa | ASTM D882 |
| 1% secant, MD, 51 µ m, blow molded film | 117 | MPa | ASTM D882 |
| tensile strength | |||
| TD, fracture, 51 µ m, blow molded film | 24.8 | MPa | ASTM D882 |
| MD, fracture, 51 µ m, blow molded film | 26.2 | MPa | ASTM D882 |
| Tensile strain | |||
| TD, fracture, 51 µ m, blow molded film | 600 | % | ASTM D882 |
| MD, fracture, 51 µ m, blow molded film | 500 | % | ASTM D882 |
| Drop hammer impact | |||
| 51 µ m, blow molded film | 310 | g | ASTM D1709 |
| tear strength | |||
| TD, 51 µ m, blow molded film | 260 | g | ASTM D1922 |
| MD, 51 µ m, blow molded film | 140 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 87.0 | ℃ | ASTM D1525 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |