| Low density moisture curable polyethylene system for low voltage building wire, control cable, photovoltaic and cable tray applications (UL styles SIS, XHH, XHHW, XHHW-2, RHH, RHW, RHW-2, PV VW-1; ‘SunRes’ and -40°C). PEXIDAN ® V/T-2UV is a low density flame-retardant XLPE system curable by moisture and consists of a silane-grafted base compound A-3001 and a catalyst masterbatch CAT-083FR-UV. Mixed and extruded in the proper proportions (50/50), the two components result in a material that is curable by exposure to hot water. PEXIDAN ® V/T-2UV is halogenated but is RoHS-compliant. Insulation made with this system may be marked SUNRES or ‘SR’ in all colors and in all sizes per UL44, UL4703 and CSA C22.2 #38. This product is also CSA-listed for RW90, RWU90, RPV90 RPVU90 and CIC, ‘SR’ and -40C rated.&& |
| Product Description | |
|---|---|
| Generic | XLPE |
| Material Status | Commercial: Active |
| Features | Crosslinked,Flame Characteristics,Low density,Halogenated |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| The degree of cross combination | 60 | % | ASTM D2765 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 13.3 | MPa | UL 1581 |
| Fracture, -5 ℃ | 12.3 | MPa | ASTM D638 |
| Fracture, 75 ℃ | 12.5 | MPa | UL 1581 |
| Tensile strain | |||
| fracture | 300 | % | UL 1581 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Change rate of ultimate elongation | |||
| 1440 hr in oil | 290 | % | |
| 23 ℃, 720 hours in oil | 320 | % | |
| Aging test | |||
| Tensile strength after exposure | 13.4 | MPa | |
| Elongation after exposure | 280 | % |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| deformation | 9.0 | % | UL 1581 |
| thermosetting | |||
| Elongation under load: 150 ℃ | 45 | % | Internal Method |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative permittivity | |||
| 90℃ | 3.10 | UL 1581 | |
| breakdown voltage | |||
| — | 30000 | V | |
| after glancing impact | 21000 | V | |
| Pass | UL 1581 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | 27 | % | ASTM D2863 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Crushing Test | 616886 | g | UL 1581 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 154 to 171 | °C | |
| Barrel 2 zone temperature | 154 to 171 | °C | |
| Barrel 3 zone temperature | 154 to 171 | °C | |
| Barrel 4 zone temperature | 154 to 171 | °C | |
| Head temperature | 185 | °C | |
| Nozzle temperature | 185 | °C | |
| Screw cooling | neutral | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 3. After 30 day gasoline |
| 4. After 60 day oil |
| 5. 15 minutes |
| 6. 720 hr. exposure – SUNRES |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |