Pharmalene® BC 82 PH

About
Pharmalene BC 82 PH is an high density polyethylene hexene copolymer, produced with gas phase technology. Its production is realized in conformity to the good manufacturing practices (GMP). The main use is in the pharmaceutical sector. The antioxidant additives used in it are approved by the polyethylene monography of the European Pharmacopoeia and used in compliance with it.The resin formulation is established by years of experience and it is not subject of changes. Pharmalene BC 82 PH is a multipurpose blow moulding material. This technology is used for manufacturing containers for solid or bottles for liquid. Pharmalene BC 82 PH, thanks to its limited gels content, can be even used for film production.&&

About

Pharmalene BC 82 PH is an high density polyethylene hexene copolymer, produced with gas phase technology. Its production is realized in conformity to the good manufacturing practices (GMP). The main use is in the pharmaceutical sector. The antioxidant additives used in it are approved by the polyethylene monography of the European Pharmacopoeia and used in compliance with it.The resin formulation is established by years of experience and it is not subject of changes. Pharmalene BC 82 PH is a multipurpose blow moulding material. This technology is used for manufacturing containers for solid or bottles for liquid. Pharmalene BC 82 PH, thanks to its limited gels content, can be even used for film production.&&

Product Description
Generic	HDPE
Material Status	Commercial: Active
Features	Food contact compliance,Inoxidizability,Copolymer,High density
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.954	g/cm³	ISO 1183
Melt Flow Rate			ISO 1133
190℃，2.16kg	0.25	g/10min	ISO 1133
190℃，21.6kg	23	g/10min	ISO 1133
190℃，5.0kg	0.90	g/10min	ISO 1133
ESCR(Environmental Stress Cracking Resistance)
Compression Molding	> 60.0	hr	ASTM D1693B

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
Compression Molding	180	J/m	ISO 180-A

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	< -60.0	℃	ASTM D746
Vicat Softening Temp	125	℃	ISO 306/A
Melting temperature	135	℃	Internal Method

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D, molded	64		ISO 868
tensile strength			ISO 527-2
Yield, molding	27.0	MPa	ISO 527-2
Fracture, molded	30.0	MPa	ISO 527-2
Tensile strain
Fracture, molded	> 600	%	ISO 527-2
Bending modulus
Compression Molding	1200	MPa	ISO 178

Process Conditions
Extrusion	Nominal value	Unit	Test method
Barrel 1 zone temperature	170 to 180	°C
Barrel 3 zone temperature	185 to 195	°C
Melt temperature	195 to 205	°C
Head temperature	185 to 190	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.