| Main Features: high mechanical properties Main Applications: unidoses, multilayer films for blisters&& |
| Product Description | |
|---|---|
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Low density |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.922 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.25 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | > 0.50 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | 60 to 250 µm | ||
| Tensile modulus | |||
| 1% secant, MD | 160 | MPa | |
| 1% secant, TD | 180 | MPa | |
| tensile strength | |||
| MD, yield | 10.0 | MPa | |
| TD, yield | 11.0 | MPa | |
| MD, fracture | 25.0 | MPa | |
| TD, fracture | 25.0 | MPa | |
| Tensile strain | |||
| MD, fracture | 400 | % | |
| TD, fracture | 550 | % | |
| Drop hammer impact | 290 | g | ISO 7765-1/B |
| Elmandorf tear strength | |||
| MD | 25 | N | |
| TD | 25 | N |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -75.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 98.0 | ℃ | ISO 306/A |
| Melting temperature | 112 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45° | 30 | ASTM D2457 | |
| Haze | 20 | % | ISO 14782 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |