Plantic® WR700

About
Plantic Technologies Limited develops and produces advanced bio-based materials. Plantic® is an innovative product made from corn-starch (maize) that is Australian grown and non-genetically modified. Plantic® is an Australian registered trademark of Plantic Technologies Limited. Plantic® WR700 is a thermoplastic starch (TPS) polymer formulated for injection molding. It has been designed to be used in applications requiring water resistance for periods of up to 12 weeks. It is suitable for molding parts with a wall thickness between 0.5 – 3.0 mm.&&

About

Plantic Technologies Limited develops and produces advanced bio-based materials. Plantic® is an innovative product made from corn-starch (maize) that is Australian grown and non-genetically modified. Plantic® is an Australian registered trademark of Plantic Technologies Limited. Plantic® WR700 is a thermoplastic starch (TPS) polymer formulated for injection molding. It has been designed to be used in applications requiring water resistance for periods of up to 12 weeks. It is suitable for molding parts with a wall thickness between 0.5 – 3.0 mm.&&

Product Description
Generic	生物可降解聚合物
Material Status	Commercial: Active
Features	Renewable resources,Biodegradable,Moisture resistance
Availabilitys	Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.35	g/cm³	ASTM D792
Shrinkage rate
MD	0.60 to 0.90	%

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	31	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	44.9	℃	ASTM D648
Vicat Softening Temp	70.2	℃	ASTM D1525

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	52		ASTM D2240
Tensile modulus	630	MPa	ASTM D638
tensile strength
yield	< 7.50	MPa	ASTM D638
Tensile strain
fracture	2.0	%	ASTM D638

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	70	°C
Drying time	3.0 to 4.0	hr
Recommended maximum moisture content	2.0 to 3.0	%
Barrel rear temperature	110 to 150	°C
Barrel middle temperature	150 to 170	°C
Barrel front temperature	160 to 180	°C
Nozzle temperature	170 to 190	°C
Processing (melt) temperature	175 to 200	°C
Mold temperature	25 to 50	°C
Back pressure	0.00 to 10.0	MPa
Screw speed	50 to 150	rpm

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.