| About |
|---|
| Plaslube® J-50/30/TF/15 is a Polycarbonate (PC) product filled with 30% glass fiber. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Engineering/Industrial Parts. Characteristics include: Flame Rated RoHS Compliant Good Dimensional Stability High Strength Lubricated&& |
| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Lubricating,Good wear resistance,HB,V-1 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.57 | g/cm³ | ASTM D792 |
| Density | 1.57 | g/cm³ | ISO 1183-2 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.20 | % | ASTM D955 |
| Water absorption rate | |||
| saturated | 0.10 | % | ISO 62-2 |
| 24hr | 0.080 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 180 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 146 | ℃ | ASTM D648 |
| 1.8 MPa | 145 | ℃ | ISO 75-2 2 |
| Linear coefficient of thermal expansion | |||
| MD | 2.7E-5 | 1/℃ | ASTM D696 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-1 | UL 94 | |
| Flame retardant level | |||
| 3.00 mm | V-1 | ISO 1210 2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 8620 | MPa | ASTM D638 |
| Tensile modulus | 10000 | MPa | ISO 527-2 2 |
| tensile strength | |||
| fracture | 120 | MPa | ISO 527-2 2 |
| 23℃ | 117 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ASTM D638 |
| fracture | 3.0 | % | ISO 527-2 2 |
| Bending modulus | |||
| 23℃ | 7580 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 165 | MPa | ASTM D790 |
| compressive strength | 110 | MPa | ASTM D695 |
| friction coefficient | |||
| Steel – Static | 0.18 | ASTM D1894 | |
| Rockwell hardness | |||
| R-level | 115 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.030 | % | |
| Barrel rear temperature | 299 to 316 | °C | |
| Barrel middle temperature | 310 to 327 | °C | |
| Barrel front temperature | 304 to 321 | °C | |
| Nozzle temperature | 304 to 321 | °C | |
| Processing (melt) temperature | 304 to 332 | °C | |
| Mold temperature | 71 to 88 | °C | |
| Injection speed | Moderate-Fast | ||
| Back pressure | 0.345 to 0.689 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |