| About |
|---|
| Plaslube® PA4/6 CF30 TL15 is a Polyamide 46 (Nylon 46) product filled with 30% carbon fiber. It can be processed by injection molding and is available in North America. Characteristics include: Flame Rated Lubricated Wear Resistant&& |
| Product Description | |
|---|---|
| Generic | PA 46 |
| Material Status | Commercial: Active |
| Features | Low coefficient of friction,Lubricating,Good wear resistance,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.43 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.40 to 0.70 | % | ASTM D955 |
| MD：3.2 mm | 0.10 to 0.30 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 2.0 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 186 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.6 | % | ASTM D638 |
| Bending modulus | 16500 | MPa | ASTM D790 |
| bending strength | 283 | MPa | ASTM D790 |
| friction coefficient | ASTM D1894 | ||
| Steel – Dynamic | 0.13 | ASTM D1894 | |
| Steel – Static | 0.12 | ASTM D1894 | |
| Wear factor | 24 | 10^-8 mm³/N·m | ASTM D3702 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 69 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 285 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 293 | ℃ | ASTM D648 |
| Melting temperature | 295 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 2.7E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 10 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 85 | °C | |
| Drying time | 4.0 to 8.0 | hr | |
| Barrel rear temperature | 282 to 316 | °C | |
| Barrel middle temperature | 282 to 316 | °C | |
| Barrel front temperature | 282 to 316 | °C | |
| Processing (melt) temperature | 246 to 316 | °C | |
| Mold temperature | 88 to 127 | °C | |
| Back pressure | 0.00 to 0.345 | MPa | |
| Screw speed | 40 to 80 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |