Plaslube® PA6/12 GF33 1000 BK

About
Plaslube® PA6/12 GF33 1000 BK is a Polyamide 612 (Nylon 612) product filled with 33% glass fiber. It can be processed by injection molding and is available in North America. Primary characteristic: flame rated.&&

Product Description
Generic	PA612
Material Status	Commercial: Active
Features	Lubricating,Heat Stabilized,HB
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.30	g/cm³	ASTM D792
Shrinkage rate
MD：3.2 mm	0.40	%	ASTM D955
Water absorption rate
24hr	0.20	%	ASTM D570

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃，3.2mm	140	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	213	℃	ASTM D648
0.45 MPa, unannealed	221	℃	ASTM D648
Linear coefficient of thermal expansion
MD	2.9E-5	1/℃	ASTM D696

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	1.0E+15	ohms·cm	ASTM D257
Dielectric strength	16	kV/mm	ASTM D149

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	HB		UL 94

MECHANICAL	Nominal value	Unit	Test method
tensile strength	152	MPa	ASTM D638
Tensile strain
fracture	6.0	%	ASTM D638
Bending modulus	6890	MPa	ASTM D790
bending strength	214	MPa	ASTM D790
Rockwell hardness
R-level	120		ASTM D785

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.