| About |
|---|
| Plaslube® PEEK CF10 TL10 GL10 A是一种聚醚醚酮(PEEK)产品,含有的填充物为玻璃、碳纤维增强材料。 它可以通过注射成型进行加工,在北美洲有供货。 主要特性为:润滑。&& |
| Product Description | |
|---|---|
| Generic | PEEK |
| Material Status | Commercial: Active |
| Features | Lubricating |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.46 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.90 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.15 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 91 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 310 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | > 316 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 2.2E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+4 to 1.0E+6 | ohms·cm | ASTM D257 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Pressure limiting speed | ASTM D3702 | ||
| 10 fpm | 40000 | psi·fpm | ASTM D3702 |
| 100 fpm | 45000 | psi·fpm | ASTM D3702 |
| 1000 fpm | 28000 | psi·fpm | ASTM D3702 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 146 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.5 | % | ASTM D638 |
| Bending modulus | 9650 | MPa | ASTM D790 |
| bending strength | 276 | MPa | ASTM D790 |
| friction coefficient | ASTM D1894 | ||
| Steel – Dynamic | 0.22 | ASTM D1894 | |
| Steel – Static | 0.19 | ASTM D1894 | |
| Wear factor | 56 | 10^-8 mm³/N·m | |
| Rockwell hardness | |||
| R-level | 116 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 249 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 360 to 388 | °C | |
| Barrel middle temperature | 360 to 388 | °C | |
| Barrel front temperature | 360 to 388 | °C | |
| Processing (melt) temperature | 360 to 382 | °C | |
| Mold temperature | 177 to 218 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |