| About |
|---|
| PLAVIS is a super engineering plastic. PLAVIS polyimide has a unique chemical structure with some of the highest properties availiable. Nitrogen bonded to 3 carbons is the critical part of the chain and imparts the plastic with remarkable features and benefits. DAELIM makes PLAVIS isostatic molded rods have uniform properties in all directions.&& |
| Product Description | |
|---|---|
| Generic | TPI |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Self-lubricating,High Heat Resistance,Low odor |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.58 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-grade, molded | 70 to 90 | ASTM D785 | |
| tensile strength | |||
| Fracture, 23 ℃ | 63.7 | MPa | ASTM D1708 |
| Tensile strain | |||
| Fracture, 23 ℃ | 4.0 | % | ASTM D1708 |
| Bending modulus | |||
| 23 ℃, molded | 3330 | MPa | |
| 260 ℃, molded | 1860 | MPa | |
| bending strength | |||
| 23 ℃, molded | 78.5 | MPa | |
| 260 ℃, molded | 44.1 | MPa | |
| Compression modulus | 2450 | MPa | ASTM D695 |
| compressive strength | |||
| 1% strain, 23 ℃ | 34.3 | MPa | |
| 10% strain, 23 ℃ | 128 | MPa | |
| Wear Rate | 2 | m/min |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Compression Molded |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |