| About |
|---|
| PLENCO 03356 is a mineral filled phenolic molding compound offering excellent arc resistance, comparative tracking, and flame resistant properties. UL recognized under component file E40654. 03356 is available in black.&& |
| Product Description | |
|---|---|
| Generic | 酚醛树脂 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Arc resistance,V-0 |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.55 | g/cm³ | ASTM D792 |
| Apparent density | 0.66 | g/cm³ | ASTM D1895 |
| Shrinkage rate | |||
| MD | 0.82 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.22 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 16.9 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | 17 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 165 | ℃ | ASTM D648 |
| Continuous use temperature | 204 | ℃ | ASTM D794 |
| Linear coefficient of thermal expansion | |||
| MD | 4.7E-5 | 1/℃ | ASTM E831 |
| Thermal conductivity coefficient | |||
| 100℃ | 0.54 | W/m/K | ASTM C177 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 8.9E+11 | ohms·cm | ASTM D257 |
| Dielectric strength | ASTM D149 | ||
| — | 11 | kV/mm | ASTM D149 |
| — | 7.6 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 MHz | 5.20 | ASTM D150 | |
| Dissipation factor | |||
| 1 MHz | 0.066 | ASTM D150 | |
| Arc resistance | 182 | sec | ASTM D495 |
| Compared to the leakage tracing index | 175 | V | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 | |
| Extreme oxygen index | 29 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| E-level | 77 | ASTM D785 | |
| Tensile modulus | 11000 | MPa | ASTM D638 |
| tensile strength | 50.7 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 0.54 | % | ASTM D638 |
| Bending modulus | 8810 | MPa | ASTM D790 |
| bending strength | 79.3 | MPa | ASTM D790 |
| compressive strength | 159 | MPa | ASTM D695 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Recommended injection volume | Nominal value | Unit | Test method |
| Barrel rear temperature | 66 to 82 | °C | |
| Barrel front temperature | 82 to 99 | °C | |
| Processing (melt) temperature | 104 to 115 | °C | |
| Mold temperature | 165 to 182 | °C | |
| Injection pressure | 6.20 to 11.0 | MPa | |
| Back pressure | 0.300 | MPa | |
| Screw speed | < 60 | rpm | |
| Cushion | 3.00 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method A (Short-Time) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |