| About |
|---|
| PLENCO 05118 is a mineral and graphite filled phenolic molding compound. Customers have found this material useful for bearing seals. 05118 provides for a low coefficient of friction, abrasion resistance, minimal water absorption, and excellent dimensional stability under severe exposure. 05118 is available in gray. 05118 is not recommended for electrical insulating applications.&& |
| Product Description | |
|---|---|
| Generic | 酚醛树脂 |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Low or no water absorption,Low coefficient of friction,Good wear resistance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.82 | g/cm³ | ASTM D792 |
| Apparent density | 0.89 | g/cm³ | ASTM D1895 |
| Shrinkage rate | |||
| MD | 0.35 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.050 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 16.1 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | 16 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 180 | ℃ | ASTM D648 |
| Continuous use temperature | 202 | ℃ | ASTM D794 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| E-level | 58 | ASTM D785 | |
| Tensile modulus | 13300 | MPa | ASTM D638 |
| tensile strength | 39.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 0.50 | % | ASTM D638 |
| Bending modulus | 11100 | MPa | ASTM D790 |
| bending strength | 64.6 | MPa | ASTM D790 |
| compressive strength | 128 | MPa | ASTM D695 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |