Plexar® PX3198

About
Plexar tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins and copolymers, EVA, EMA, polypropylene, polyamide (nylon), ethylene vinyl alcohol copolymers (EVOH), ionomer and other sealants, polyethylene terephthalate (PET) resins and copolymers, styrenic polymers, metal, and paperboard. Product grades primarily used for blown and cast films, sheet and thermoforming, blow molding, extrusion coating and lamination, tubing, pipe, and other specialty applications are available in pellet form. Contact your Plexar sales and/or Equistar technical service representative for more information and specific recommendations for your application(s).

About

Plexar tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins and copolymers, EVA, EMA, polypropylene, polyamide (nylon), ethylene vinyl alcohol copolymers (EVOH), ionomer and other sealants, polyethylene terephthalate (PET) resins and copolymers, styrenic polymers, metal, and paperboard. Product grades primarily used for blown and cast films, sheet and thermoforming, blow molding, extrusion coating and lamination, tubing, pipe, and other specialty applications are available in pellet form. Contact your Plexar sales and/or Equistar technical service representative for more information and specific recommendations for your application(s).

Product Description
Supplier	LyondellBasell
Generic	Linear low density polyethylene
Material Status	Commercial: Active
Features	Low density
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.933	g/cm³	ASTM D1505
Melt Flow Rate
190℃，2.16kg	2.7	g/10min	ASTM D1238

film	Nominal value	Unit	Test method
film thickness	51	µm
Tensile strength
MD: Yield	14.3	MPa
TD: Yield	16.7	MPa
MD: Fracture	29.4	MPa
TD: Fracture	22.5	MPa
Tensile strain
MD, yield	12	%
TD, yield	10	%
MD, fracture	700	%
TD, fracture	730	%
Elmandorf tear strength
MD	63	g
TD	610	g
Water vapor transmittance (51 µ m, 38 ° C, 100% RH)	6.3	g·mm/m²/atm/24 hr	ASTM F372

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	109	℃	ASTM D1525

Process Conditions
extrusion	Nominal value	Unit	Test method
Melt Temperature	210	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.