Plexiglas® Hi-Gloss FT15 black 9V022

About
PLEXIGLAS® Hi-Gloss FT15 black 9V022 is a special acrylic-based polymer. With regard to its high mar resistance good weather resistance good polishability, PLEXIGLAS® Hi-Gloss FT15 9V022 shows comparable properties to those of PLEXIGLAS® standard molding compounds. In addition, PLEXIGLAS® Hi-Gloss FT15 9V022 offers the special benefit of a high heat deflection temperature combined with good flow. Application: PLEXIGLAS® Hi-Gloss FT15 9V022 is particularly suitable for injection molding technical components. Owing to ist superior brilliance, high-gloss (Class A) black surfaces can be obtained in. Examples: add-on automotive body parts&&

About

PLEXIGLAS® Hi-Gloss FT15 black 9V022 is a special acrylic-based polymer. With regard to its high mar resistance good weather resistance good polishability, PLEXIGLAS® Hi-Gloss FT15 9V022 shows comparable properties to those of PLEXIGLAS® standard molding compounds. In addition, PLEXIGLAS® Hi-Gloss FT15 9V022 offers the special benefit of a high heat deflection temperature combined with good flow. Application: PLEXIGLAS® Hi-Gloss FT15 9V022 is particularly suitable for injection molding technical components. Owing to ist superior brilliance, high-gloss (Class A) black surfaces can be obtained in. Examples: add-on automotive body parts&&

Product Description
Supplier	ROHM
Generic	PMMA
Material Status	Commercial: Active
Features	Weather resistance is good,Good surface appearance,Good liquidity,High Heat Resistance
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.19	g/cm³	ISO 1183
Melt Volume Rate
230℃，3.8 kg	4.50	cm³/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	3500	MPa	ISO 527-1-2
tensile strength
fracture	50.0	MPa	ISO 527-2/5
Tensile strain
fracture	3.1	%	ISO 527-2/5

IMPACT	Nominal value	Unit	Test method
Charpy Unnotch Impact strength
23℃	18	kJ/m²	ISO 179/1eU

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	107	℃	ISO 75-2/B
1.8 MPa, unannealed	105	℃	ISO 75-2/A
Glass transition temperature	121	℃	ISO 11357-2
Vicat Softening Temp
B50	115	℃	ISO 306

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Igniting temperature of the hot wire	675	℃	IEC 60695-2-13

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	100	°C
Drying time	4.0 to 6.0	hr
Processing (melt) temperature	220 to 250	°C
Mold temperature	70 to 95	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.