| About |
|---|
| Product Description | |
|---|---|
| Supplier | ROHM |
| Material Status | Commercial: Active |
| Features | High impact resistance,High ESCR,weathering resistance,Good Clarity |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Volume Rate | |||
| 230℃，3.8 kg | 3.0 | cm³/10min | ISO 1133 |
| Density | 1.17 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | |||
| 1 mm/min | 2200 | MPa | ISO 527 |
| Tensile Strength | |||
| Yield yld, 50 mm/min | 55 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield yld, 50 mm/min | 5 | % | ISO 527 |
| Elongation at Break | |||
| 50 mm/min | 28 | % | ISO 527 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | 70 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temperature | 93 | ℃ | ISO 306/B |
| Hot deformation temperature HDT | |||
| 0.45 MPa | 90 | ℃ | ISO 75-1/-2 |
| OPTICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Light Transmission | 91 | % | ISO 13468-2 |
| Haze | <2 | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | <90 | ℃ | |
| Drying Time | 2-3 | hr | |
| Melt Temperature | 220-260 | ℃ | |
| Mold Temperature | 50-70 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |