| About |
|---|
| PLEXIGLAS® Satinice df22 zk6BR, based on PLEXIGLAS® Resist zk6BR, is an impact modified molding compound characterized by diffuse scattering of light. Typical properties of impact modified PLEXIGLAS® molding compound are high break resistance and impact strength improved resistance to stress cracking good weather resistance high surface hardness and mar resistance the pleasant feel and sound of the moldings. PLEXIGLAS® Satinice df22 zk6BR is characterized by the following special properties: very good lightdiffusion combined with excellent light transmission matte surfaces can be obtained by varying the extrusion parameters. Application: Used for extruding profiles and sheets, but also for injection molding items for lighting engineering applications Examples: applications that call for light diffusion combined with optimum transmission&& |
| Product Description | |
|---|---|
| Supplier | ROHM |
| Generic | PMMA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,High impact resistance,Good Hardness,High ESCR |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 230℃，3.8 kg | 1.40 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1800 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 45.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 5.0 | % | ISO 527-2/50 |
| Nominal tensile fracture strain | 40 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.5 | kJ/m² | ISO 179/1 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 54 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 99.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 93.0 | ℃ | ISO 75-2/A |
| Glass transition temperature | 109 | ℃ | ISO 11357-2 |
| Vicat Softening Temp | |||
| B50 | 98.0 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD：0~50℃ | 9.0E-5 | 1/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Igniting temperature of the hot wire | 700 | ℃ | IEC 60695-2-13 |
| Flame retardant level | B2 | DIN 4102 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | 86.0 | % | ISO 13468-2 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Half（Value Angle） | 12.5 | ° | DIN 5036 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | < 85 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Melt temperature | 230 to 260 | °C | |
| Nozzle temperature | 260 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |