| PLEXIGLAS® Mineral BV is a new generation of mineral materials. The patented product PLEXIGLAS® Mineral BV (a combination of acrylic resin and mineral filler) offers unique thermoforming properties combined with a finished satin or gloss surface, in very large sizes. Like no other material before, PLEXIGLAS® Mineral BV unites the benefits of this class of material with the flexibility of PLEXIGLAS®. Owing to these properties, PLEXIGLAS® Mineral BV is suitable for both horizontal and vertical applications in indoor and outdoor areas. Indoors: Wall panels/wall protection Wet rooms: bathrooms and spas Shelves, window sills, furniture Sanitaryware such as bathtubs and shower solutions, washstands Displays, signs Platforms Outdoors : Facades/wall paneling Window sill and decor profiles Objects of all kinds&& |
| Product Description | |
|---|---|
| Supplier | ROHM |
| Generic | PMMA |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good surface appearance,Clean,Low or no water absorption,Good Printability,Solvent resistance |
| Availabilitys | Europe |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.54 | g/cm³ | ISO 1183 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 1.1 | kJ/m² | ISO 179-1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | > 105 | ℃ | ISO 306/B |
| Linear coefficient of thermal expansion | |||
| MD | 5.0E-5 | 1/℃ | DIN 53752-A |
| Hot deformation temperature | 100 to 108 | ℃ | ISO 75-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| — | E | EN 13501-1 | |
| — | B2 | DIN 4102 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Falling ball impact test | > 180.00 | cm | EN 483-2 |
| Distortion | Internal Method | ||
| Crosswise | < 0.19 | % | Internal Method |
| Longitudinal | < 0.19 | % | Internal Method |
| Thickness tolerance | 5.00 to 7.00 7.20 to 8.80 9.00 to 11.0 10.8 to 13.2 | mm | |
| Weight per Unit Area（8.00 mm） | 12.3 | kg/m² | |
| Forming temperature | |||
| 2D | > 140 | ℃ | |
| 3D | 160 to 210 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Babbitt hardness | 50 to 70 | DIN EN 59 | |
| tensile strength | > 40.0 | MPa | ISO 527-2/1B/5 |
| Tensile strain | |||
| fracture | < 2.1 | % | ISO 527-2/1B/5 |
| Bending modulus | > 4700 | MPa | ISO 178 |
| bending strength | > 78.0 | MPa | ISO 178 |
| Taber abraser | 145 to 160 | mg | DIN 14688 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |