| About |
|---|
| PLEXIGLAS® Solar 0Z023 is an extruded acrylic sheet material (polymethyl methacrylate, PMMA) that is highly weather-resistant and transparent. Special Properties UV transmission is specially adjusted to photovoltaics applications (PV, CPV), providing better energy conversion efficiency and module efficiency, and longer service life of photo cells, lenses and covers Other Typical Properties high mechanical strength, surface hardness and scratch resistance ease of processing good thermoformability high heat deflection temperature greater impact strength than glass combined with much lighter weight Applications Covers for build-in photovoltaics Hot embossing of radial and linear Fresnel lenses for CPV/CSP applications&& |
| Product Description | |
|---|---|
| Supplier | ROHM |
| Generic | PMMA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Excellent Processability,Good Hardness,High scratch resistance,HB |
| Availabilitys | Europe |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 23℃，24hr | 38.0 | mg | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 20 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 103 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 98.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 108 | ℃ | ISO 306/B |
| Linear coefficient of thermal expansion | |||
| MD：0~50℃ | 8.0E-5 | 1/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 | |
| Flame retardant level | B2 | DIN 4102 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.490 | ISO 489 | |
| Transmittance | 92.0 | % | ISO 13468-2 |
| Haze | < 0.50 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Weight gain | |||
| during immersion | < 2.1 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | 183 | MPa | ISO 2039-1 |
| Tensile modulus | 3300 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 77.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 5.5 | % | ISO 527-2/5 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |