PLUSTEK PA320G6

About
30% GLASS-FIBER REINFORCED, FLAME RETARDANT POLYAMIDE 6.6 FOR INJECTION MUOLDING APPLICATIONS.&&

Product Description
Supplier	Ram-On
Generic	PA66
Material Status	Commercial: Active
Features	Flame Characteristics,V-0
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.38	g/cm³	ASTM D792
Density	1.38	g/cm³	ISO 1183
Shrinkage rate	0.30 to 0.70	%	ISO 2577
MD	0.30 to 0.70	%	ASTM D955
Water absorption rate
Saturation, 23 ℃	4.5	%	ISO 62
saturated	4.5	%	ASTM D570
Equilibrium, 23 ℃, 50% RH	1.5	%	ASTM D570
Equilibrium, 23 ℃, 50% RH	1.5	%	ISO 62

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	110	J/m	ASTM D256
23℃	12	kJ/m²	ISO 180

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	225	℃	ISO 75-2/A
1.8 MPa, unannealed	225	℃	ASTM D648
0.45 MPa, unannealed	238	℃	ASTM D648
0.45 MPa, unannealed	238	℃	ISO 75-2/B
Melting peak temperature	256	℃	ASTM D3417
Melting temperature	256	℃	ISO 11357-3

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	1.0E+13	ohms	IEC 60093
Volume resistivity	1.0E+17	ohms·cm	IEC 60093
Dielectric strength	80	kV/mm	IEC 60243-1
Dielectric constant
1 MHz	3.70		IEC 60250
Compared to the leakage tracing index	325	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level			UL 94
1.60 mm	V-0		UL 94
3.00 mm	V-0		UL 94
Glowing wire flammability index
1.6 mm	960	℃	IEC 60695-2-12
Igniting temperature of the hot wire
1.6 mm	825	℃	IEC 60695-2-13

MECHANICAL	Nominal value	Unit	Test method
tensile strength
yield	150	MPa	ISO 527-2
yield	150	MPa	ASTM D638
Tensile strain
fracture	2.0	%	ASTM D638
fracture	2.0	%	ISO 527-2
Bending modulus	8000	MPa	ASTM D790
Bending modulus	8000	MPa	ISO 178
bending strength	200	MPa	ASTM D790
bending strength	200	MPa	ISO 178
Rockwell hardness
R-level	122		ASTM D785
R-level	122		ISO 2039-2

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	85	°C
Drying time	3.0	hr
Recommended maximum moisture content	0.15	%
Barrel rear temperature	270 to 280	°C
Barrel middle temperature	280 to 300	°C
Barrel front temperature	285 to 310	°C
Mold temperature	65 to 110	°C
Injection pressure	70.0 to 125	MPa
Injection speed	Fast
Hold pressure	35.0 to 85.0	MPa
Back pressure	0.350 to 0.700	MPa
Screw speed	60 to 90	rpm

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.