POCAN® B1301 000000

soliao
2024年4月11日
PBT

About
POCAN® B1301 000000 PBT, non-reinforced, injection molding, suitable for food-contact&&POCAN® B1301 000000 PBT, non-reinforced, injection molding, suitable for food-contact&&POCAN® B1301 000000 PBT, non-reinforced, injection molding, suitable for food-contact&&

Product Description
Supplier	LANXESS
Generic	polybutylene terephthalate
Material Status	Commercial: Active
Features	Food contact compliance
Availabilitys	North America,Latin America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.31	g/cm³	ISO 1183
Apparent density	0.80	g/cm³	ISO 60
Melt Volume Rate
260℃，2.16 kg	60.0	cm³/10min	ISO 1133
Shrinkage rate
TD：120℃，2.0 mm	0.30	%
TD：260℃，2.0 mm	1.8	%
MD：120℃，2.0 mm	0.30	%
MD：260℃，2.0 mm	1.8	%
Water absorption rate
Saturation, 23 ℃	0.50	%
Equilibrium, 23 ℃, 50% RH	0.20	%
Viscosity value
Reduced viscosity	105.0	ml/g	ISO 1628

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
-30℃	< 10	kJ/m²
Charpy Unnotch Impact strength
-30℃	150	kJ/m²
23℃	180	kJ/m²
Impact strength of cantilever beam notch
-40℃	< 10	kJ/m²
23℃	< 10	kJ/m²
Notched impact strength of cantilever beam
-30℃	90	kJ/m²
23℃	130	kJ/m²
Multi axial instrumented impact energy
23 ℃, energy to peak strength	110	J	ISO 6603-2

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	140	℃	ISO 75-2/B
1.8 MPa, unannealed	65.0	℃	ISO 75-2/A
Vicat Softening Temp
B120	180	℃	ISO 306/B120
Ball pressure test
190℃	通过		IEC 60695-10-2
Melting temperature	225	℃	ISO 11357-3
Linear coefficient of thermal expansion
MD：23~55℃	1.1E-4	1/℃
TD：23~55℃	1.1E-4	1/℃
Thermal conductivity coefficient
23℃	0.25	W/m/K	ISO 8302

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	> 1.0E+15	ohms	IEC 60093
Volume resistivity
23℃	> 1.0E+15	ohms·cm	IEC 60093
Dielectric strength
23 ℃，1 mm	30	kV/mm	IEC 60243-1
Relative permittivity
23℃，100 Hz	3.40
23℃，1 MHz	3.20
Dissipation factor
23℃，100 Hz	1.5E-3
23℃，1 MHz	0.019
Compared to the leakage tracing index
Solution A	600	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level
0.75 mm	HB
1.50 mm	HB
Glowing wire flammability index
2.0 mm	750	℃	IEC 60695-2-12
Extreme oxygen index	24	%	ISO 4589-2

Supplementary information	Nominal value	Unit	Test method
Electrolytic corrosion
23℃	A 1		IEC 60426
ISO Shortname	ISO 7792-1-PBT, GR, 09-030

MECHANICAL	Nominal value	Unit	Test method
Ball hardness	120	MPa	ISO 2039-1
Tensile modulus
23℃	2700	MPa	ISO 527-1-2
tensile strength
Yield, 23 ℃	60.0	MPa	ISO 527-2/50
Tensile strain
Yield, 23 ℃	9.0	%	ISO 527-2/50
Nominal tensile fracture strain
23℃	> 10	%	ISO 527-2/50
Tensile creep modulus
1 hr	2400	MPa
1000 hr	1400	MPa
Bending modulus
23℃	2650	MPa	ISO 178-A
bending strength
23℃	90.0	MPa
3.50% strain, 23 ℃	80.0	MPa
Bending strain	6.0	%	ISO 178/A

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature – Dehumidifying desiccant	120	°C
Drying time – Dehumidifying desiccant	4.0 to 8.0	hr
Processing (melt) temperature	250 to 270	°C
Mold temperature	80 to 100	°C
Residual Moisture Content	0.0 to 0.020	%	Karl Fisher

Notes
1. Typical properties: these are not to be construed as specifications.
2. 60x60x2mm, 4 hr
3. 60x60x2mm, 80°C MT, 600 bar
4. 0.079 in/min
5. 2 mm/min
6. 10°C/min
7. Procedure A
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.