POCAN® DP 1105 000000

soliao
2024年4月9日
PBT

About
POCAN® DP1105 000000 PBT, non-reinforced, injection molding, improved flowability&&POCAN® DP1105 000000 PBT, non-reinforced, injection molding, improved flowability&&POCAN® DP1105 000000 PBT, non-reinforced, injection molding, improved flowability&&

Product Description
Supplier	LANXESS
Generic	polybutylene terephthalate
Material Status	Commercial: Active
Features	Good liquidity,HB
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.31	g/cm³	ISO 1183
Apparent density	0.80	g/cm³	ISO 60
Melt Volume Rate
250℃，1.2 kg	42.0	cm³/10min	ISO 1133
Shrinkage rate			ISO 294-4
TD：250℃，2.0 mm	2.4	%	ISO 294-4
TD：120℃，2.0 mm，2 hrs	0.10	%	ISO 294-4
MD：250℃，2.0 mm	2.2	%	ISO 294-4
MD：120℃，2.0 mm，2 hrs	0.30	%	ISO 294-4
Water absorption rate
Saturation, 23 ℃	0.50	%	ISO 62
Equilibrium, 23 ℃, 50% RH	0.20	%	ISO 62

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179/1eA
-30℃	< 10	kJ/m²	ISO 179/1eA
23℃	< 10	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength			ISO 179/1eU
-30℃	110	kJ/m²	ISO 179/1eU
23℃	140	kJ/m²	ISO 179/1eU
Impact strength of cantilever beam notch			ISO 180/1A
-30℃	< 10	kJ/m²	ISO 180-1A
23℃	< 10	kJ/m²	ISO 180-1A
Notched impact strength of cantilever beam			ISO 180/1U
-30℃	70	kJ/m²	ISO 180/1U
23℃	80	kJ/m²	ISO 180/1U

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	65.0	℃	ISO 75-2/A
0.45 MPa, unannealed	160	℃	ISO 75-2/B
Vicat Softening Temp
B120	185	℃	ISO 306/B120
Melting temperature	223	℃	ISO 11357-3
Linear coefficient of thermal expansion
TD：23~55℃	1.0E-4	1/℃	ISO 11359-2
MD：23~55℃	1.0E-4	1/℃	ISO 11359-2

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	1.0E+17	ohms	IEC 60093
Volume resistivity
23℃	1.0E+16	ohms·cm	IEC 60093
Dielectric strength
23 ℃，1 mm	30	kV/mm	IEC 60243-1
Relative permittivity			IEC 60250
23℃，100 Hz	3.40		IEC 60250
23℃，1 MHz	3.20		IEC 60250
Dissipation factor			IEC 60250
23℃，100 Hz	1.4E-3		IEC 60250
23℃，1 MHz	0.022		IEC 60250
Compared to the leakage tracing index
Solution A	350	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level			UL 94
0.75 mm	HB		UL 94
1.60 mm	HB		UL 94
Glowing wire flammability index
2.0 mm	700	℃	IEC 60695-2-12
Extreme oxygen index	25	%	ISO 4589-2

Supplementary information	Nominal value	Unit	Test method
ISO Shortname	PBT, GHMR, 07-030		ISO 7792

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
23℃	2850	MPa	ISO 527-1-2
tensile strength
Yield, 23 ℃	65.0	MPa	ISO 527-2/50
Tensile strain
Yield, 23 ℃	9.0	%	ISO 527-2/50
Nominal tensile fracture strain
23℃	10	%	ISO 527-2/50
Bending modulus
23℃	2750	MPa	ISO 178-A
bending strength
3.50% strain	80.0	MPa	ISO 178-A
23℃	90.0	MPa	ISO 178
Bending strain	6.5	%
Ball hardness	145	MPa	ISO 2039-1

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature – Dehumidifying desiccant	120	°C
Drying time – Dehumidifying desiccant	4.0 to 8.0	hr
Processing (melt) temperature	250 to 260	°C
Mold temperature	80 to 100	°C
Residual Moisture Content	0.0 to 0.020	%

Notes
1. Typical properties: these are not to be construed as specifications.
2. 60x60x2mm, 4 hr
3. 60x60x2mm, 80°C MT, 600 bar
4. 0.079 in/min
5. 2 mm/min
6. 10°C/min
7. Procedure A
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.