| POCAN® DP2004 000000 PBT, non-reinforced, injection molding, halogen free flame retardant&&POCAN® DP2004 000000 PBT, non-reinforced, injection molding, halogen free flame retardant&&POCAN® DP2004 000000 PBT, non-reinforced, injection molding, halogen free flame retardant&& |
| Product Description | |
|---|---|
| Supplier | LANXESS |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,V-2 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.32 | g/cm³ | ISO 1183 |
| Apparent density | 0.80 | g/cm³ | ISO 60 |
| Melt Volume Rate | |||
| 250℃，2.16 kg | 55.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 2577 | ||
| TD：250℃，2.0 mm | 2.3 | % | ISO 2577 |
| TD：120℃，2.0 mm，4 hrs | 0.10 | % | ISO 2577 |
| MD：250℃，2.0 mm | 2.3 | % | ISO 2577 |
| MD：120℃，2.0 mm，4 hrs | 0.20 | % | ISO 2577 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 75 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23℃ | < 10 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 65 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 75.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 160 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| B120 | 185 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 202℃ | Pass | IEC 60695-10-2 | |
| Melting temperature | 224 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD：23~55℃ | 1.2E-4 | 1/℃ | ISO 11359-2 |
| MD：23~55℃ | 1.2E-4 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | |||
| 23℃ | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 23 ℃，1 mm | 30 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | PLC 0 | UL 746 | |
| Compared to the leakage tracing index | |||
| Solution A | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | V-2 | UL 94 | |
| 1.50 mm | V-2 | UL 94 | |
| 3.00 mm | V-2 | UL 94 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 0.40 mm | 960 | ℃ | IEC 60695-2-12 |
| 0.75 mm | 960 | ℃ | IEC 60695-2-12 |
| 1.5 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 0.75 mm | 800 | ℃ | IEC 60695-2-13 |
| 1.5 mm | 800 | ℃ | IEC 60695-2-13 |
| 3 mm | 800 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 28 | % | ISO 4589-2 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | PBT, GFHMR, 09-020 | ISO 7792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 2300 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Yield, 23 ℃ | 55.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Yield, 23 ℃ | 8.0 | % | ISO 527-2/50 |
| Nominal tensile fracture strain | |||
| 23℃ | 10 | % | ISO 527-2/50 |
| Bending modulus | |||
| 23℃ | 2100 | MPa | ISO 178-A |
| bending strength | ISO 178/A | ||
| 3.50% strain, 23 ℃ | 60.0 | MPa | ISO 178-A |
| 23℃ | 75.0 | MPa | ISO 178-A |
| Bending strain | 6.5 | % | ISO 178/A |
| Ball hardness | 120 | MPa | ISO 2039-1 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – Dehumidifying desiccant | 120 | °C | |
| Drying time – Dehumidifying desiccant | 4.0 to 8.0 | hr | |
| Processing (melt) temperature | 240 to 260 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Admissible Residence Time at Tmax | < 5.0 | min | |
| Residual Moisture Content | 0.0 to 0.020 | % | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 60x60x2mm, 4 hr |
| 3. 60x60x2mm, 80°C MT, 600 bar |
| 4. 0.079 in/min |
| 5. 2 mm/min |
| 6. 10°C/min |
| 7. Solution A |
| 8. Procedure A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |