| About |
|---|
| POCAN® DP C 1502 000000 PBT+PC, non-reinforced, injection molding, improved impact strength, low tendency to warp, UV-stabilized&& |
| Product Description | |
|---|---|
| Supplier | LANXESS |
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Low warping,High impact resistance,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 270℃，5 kg | 35.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD：250℃，2.0 mm | 1.2 | % | ISO 294-4 |
| MD：250℃，2.0 mm | 1.2 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 2100 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Yield, 23 ℃ | 50.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Yield, 23 ℃ | 3.8 | % | ISO 527-2/50 |
| Nominal tensile fracture strain | |||
| 23℃ | > 40 | % | ISO 527-2/50 |
| Bending modulus | |||
| 23℃ | 2100 | MPa | ISO 178-A |
| bending strength | |||
| 3.50% strain | 65.0 | MPa | ISO 178-A |
| 23℃ | 75.0 | MPa | ISO 178 |
| Bending strain | 5.5 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 19 | kJ/m² | ISO 179/1eA |
| 23℃ | 60 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | No Break | ISO 179/1eU | |
| 23℃ | No Break | ISO 179/1eU | |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 17 | kJ/m² | ISO 180-1A |
| 23℃ | 60 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | No Break | ISO 180/1U | |
| 23℃ | No Break | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 70.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 105 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| B120 | 125 | ℃ | ISO 306/B120 |
| Melting temperature | 225 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD：23~55℃ | 1.1E-4 | 1/℃ | ISO 11359-2 |
| MD：23~55℃ | 1.1E-4 | 1/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | HB | UL 94 | |
| Glowing wire flammability index | |||
| 4.0 mm | 750 | ℃ | IEC 60695-2-12 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | PBT+PC, GHLMPR, 11-020 | ISO 7792 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – Dehumidifying desiccant | 120 | °C | |
| Drying time – Dehumidifying desiccant | 4.0 to 8.0 | hr | |
| Processing (melt) temperature | 250 to 265 | °C | |
| Mold temperature | 60 to 90 | °C | |
| Residual Moisture Content | 0.0 to 0.020 | % | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |