| About |
|---|
| POCAN® KU2-7317 000000 PBT, 17 % white pigments, injection molding, improved light reflection, low tendency to warp, improved impact strength&&POCAN® KU2-7317 000000 PBT, 17 % white pigments, injection molding, improved light reflection, low tendency to warp, improved impact strength&&POCAN® KU2-7317 000000 PBT, 17 % white pigments, injection molding, improved light reflection, low tendency to warp, improved impact strength&& |
| Product Description | |
|---|---|
| Supplier | LANXESS |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Low warping,High impact resistance,High reflectivity,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.45 | g/cm³ | ISO 1183 |
| Apparent density | 0.90 | g/cm³ | ISO 60 |
| Melt Volume Rate | |||
| 260℃，2.16 kg | 18.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD：260℃，2.0 mm | 1.9 | % | ISO 294-4 |
| TD：120℃，2.0 mm，2 hrs | 0.30 | % | ISO 294-4 |
| MD：260℃，2.0 mm | 1.9 | % | ISO 294-4 |
| MD：120℃，2.0 mm，2 hrs | 0.30 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.40 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 2500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 40.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| Fracture, 23 ℃ | 15 | % | ISO 527-2/5 |
| Bending modulus | |||
| 23℃ | 2600 | MPa | ISO 178-A |
| bending strength | |||
| 3.50% strain | 70.0 | MPa | ISO 178-A |
| 23℃ | 75.0 | MPa | ISO 178 |
| Bending strain | 5.8 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | < 10 | kJ/m² | ISO 179/1eA |
| 23℃ | < 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 90 | kJ/m² | ISO 179/1eU |
| 23℃ | 140 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -40℃ | < 10 | kJ/m² | ISO 180-1A |
| -30℃ | < 10 | kJ/m² | ISO 180-1A |
| 23℃ | < 10 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | 60 | kJ/m² | ISO 180/1U |
| 23℃ | 130 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 60.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 140 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| B120 | 160 | ℃ | ISO 306/B120 |
| Melting temperature | 225 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD：23~55℃ | 1.1E-4 | 1/℃ | ISO 11359-2 |
| MD：23~55℃ | 1.1E-4 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | |||
| Solution A | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.80 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | PBT, GHMPR, 09-020, MD17 | ISO 7792 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 60x60x2mm, 4 hr |
| 3. 60x60x2mm, 80°C MT, 600 bar |
| 4. 0.079 in/min |
| 5. 2 mm/min |
| 6. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |