| POCAN® KU1-7625LT 904040 PBT+PC, 20 % glass fibers, injection molding, low tendency to warp, improved surface finish, improved laser-transparency, NIR-laser transparent coloring (black)&&POCAN® KU1-7625LT 904040 PBT+PC, 20 % glass fibers, injection molding, low tendency to warp, improved surface finish, improved laser-transparency, NIR-laser transparent coloring (black)&&POCAN® KU1-7625LT 904040 PBT+PC, 20 % glass fibers, injection molding, low tendency to warp, improved surface finish, improved laser-transparency, NIR-laser transparent coloring (black)&& |
| Product Description | |
|---|---|
| Supplier | LANXESS |
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | Low warping,Good surface appearance |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 | g/cm³ | ISO 1183 |
| Apparent density | 0.70 | g/cm³ | ISO 60 |
| Melt Volume Rate | |||
| 260℃，5 kg | 40.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD：110℃，3.0 mm | 0.20 | % | |
| TD：260℃，3.0 mm | 0.50 | % | |
| MD：110℃，3.0 mm | 0.15 | % | |
| MD：260℃，3.0 mm | 0.45 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.30 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.10 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 5100 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 75.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| Fracture, 23 ℃ | 4.0 | % | ISO 527-2/5 |
| Bending modulus | |||
| 23℃ | 4700 | MPa | ISO 178-A |
| bending strength | |||
| 23℃ | 130 | MPa | ISO 178-A |
| Bending strain | 4.5 | % | ISO 178/A |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 35 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| -40℃ | < 10 | kJ/m² | |
| -30℃ | < 10 | kJ/m² | |
| 23℃ | < 10 | kJ/m² | |
| Notched impact strength of cantilever beam | |||
| 23℃ | 30 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 110 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B120 | 145 | ℃ | ISO 306/B120 |
| Melting temperature | 225 | ℃ | ISO 11357-3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | HB | ||
| 1.50 mm | HB |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Gottfert Melt Viscosity（260℃） | 400 | Pa·s | Internal Method |
| ISO Shortname | ISO 7792-1-PBT+PC,GHMR,09-050,GF20 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 150x105x3mm, 1 hr |
| 3. 150x105x3mm, 80°C MT, 600 bar |
| 4. 0.079 in/min |
| 5. 2 mm/min |
| 6. 10°C/min |
| 7. 165 1/s |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |