| About |
|---|
| PBT+ASA, 15 % glass fibers, injection molding, low tendency to warp, improved surface finish&& |
| Product Description | |
|---|---|
| Supplier | LANXESS |
| Generic | PBT+ASA |
| Material Status | Commercial: Negative |
| Features | Low warping,Good surface appearance,HB |
| Availabilitys | Africa & Middle East ,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.39 | g/cm³ | ISO 1183 |
| Apparent density | 0.80 | g/cm³ | ISO 60 |
| Melt Volume Rate | |||
| 270℃，5 kg | 55.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 2577 | ||
| TD：270℃，2.0 mm | 0.70 | % | ISO 2577 |
| TD：120℃，2.0 mm，4 hrs | 0.30 | % | ISO 2577 |
| MD：270℃，2.0 mm | 0.40 | % | ISO 2577 |
| MD：120℃，2.0 mm，4 hrs | 0.20 | % | ISO 2577 |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.40 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.10 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 40 | kJ/m² | ISO 179/1eU |
| 23℃ | 50 | kJ/m² | ISO 179/1eU |
| Notched impact strength of cantilever beam | |||
| 23℃ | 40 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 210 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 150 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B120 | 165 | ℃ | ISO 306/B120 |
| Melting temperature | 225 to 250 | ℃ | ISO 11357-3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.80 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | PBT+PET+ASA, GHMR, 09-060, GF15 | ISO 7792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | 150 | MPa | ISO 2039-1 |
| Tensile modulus | |||
| 23℃ | 6000 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 100 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.5 | % | ISO 527-2/5 |
| Bending modulus | |||
| 23℃ | 5200 | MPa | ISO 178-A |
| bending strength | |||
| 23℃ | 150 | MPa | ISO 178-A |
| Bending strain | 3.2 | % | ISO 178/A |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – Dehumidifying desiccant | 120 | °C | |
| Drying time – Dehumidifying desiccant | 4.0 to 8.0 | hr | |
| Processing (melt) temperature | 260 to 280 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Residual Moisture Content | 0.0 to 0.020 | % | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |