| About |
|---|
| POCAN® TS3220 901510 PBT+PET, 20 % glass fibers, injection molding, improved impact strength, low tendency to warp, improved surface finish&&POCAN® TS3220 901510 PBT+PET, 20 % glass fibers, injection molding, improved impact strength, low tendency to warp, improved surface finish&&POCAN® TS3220 901510 PBT+PET, 20 % glass fibers, injection molding, improved impact strength, low tendency to warp, improved surface finish&& |
| Product Description | |
|---|---|
| Supplier | LANXESS |
| Generic | PBT+PET |
| Material Status | Commercial: Active |
| Features | Low warping,Good surface appearance |
| Availabilitys | Africa & Middle East ,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.38 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 270℃，5 kg | 18.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD：120℃，2.0 mm | 0.10 | % | |
| TD：270℃，2.0 mm | 0.70 | % | |
| MD：120℃，2.0 mm | 0.10 | % | |
| MD：270℃，2.0 mm | 0.40 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 5500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 75.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ISO 527-2/5 |
| Bending modulus | |||
| 23℃ | 5200 | MPa | ISO 178-A |
| bending strength | |||
| 23℃ | 120 | MPa | ISO 178-A |
| Bending strain | 3.9 | % | ISO 178/A |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | < 10 | kJ/m² | |
| 23℃ | < 10 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 45 | kJ/m² | |
| 23℃ | 50 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| -30℃ | < 10 | kJ/m² | |
| 23℃ | < 10 | kJ/m² | |
| Notched impact strength of cantilever beam | |||
| -30℃ | 40 | kJ/m² | |
| 23℃ | 40 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 215 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 155 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B120 | 130 | ℃ | ISO 306/B120 |
| Melting temperature | 225 to 250 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD：23~55℃ | 3.0E-5 | 1/℃ | |
| TD：23~55℃ | 1.3E-4 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | |||
| Solution A | 250 | V | IEC 60112 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | ISO 7792-1-PBT+PET, GHLMPR, 09-060, GF20 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – Dehumidifying desiccant | 120 | °C | |
| Drying time – Dehumidifying desiccant | 4.0 to 8.0 | hr | |
| Processing (melt) temperature | 260 to 280 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Residual Moisture Content | 0.0 to 0.020 | % | Karl Fisher |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 60x60x2mm, 4 hr |
| 3. 60x60x2mm, 90°C MT, 600 bar |
| 4. 0.079 in/min |
| 5. 2 mm/min |
| 6. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |