| About |
|---|
| POLIDAN® T/A-LX 是一种硅烷交联PE化合物，与催化剂母料一起使用，以加速交联反应。用于柔性交联管道。 应用： POLIDAN® T/A-LX用于生产家庭用热水及冷水供应管道，包括直接加热用管道的生产。该复合物专门开发用于单层和复合管道解决方案。&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | XLPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Crosslinked,High density |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.945 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，5.0kg | 1.5 | g/10min | ISO 1133 |
| Gel content | |||
| Crosslinking level | > 65 | % | EN 579 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 720 | MPa | ISO 527-2 |
| tensile strength | > 20.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 350 | % | ASTM D638 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 126 | ℃ | ASTM D1525 |
| Linear coefficient of thermal expansion | |||
| MD：20℃ | 1.9E-4 | 1/℃ | ASTM D696 |
| specific heat | |||
| 23℃ | 1900 | J/kg/℃ | ISO 11357 |
| Thermal conductivity coefficient | |||
| 23℃ | 0.45 to 0.47 | W/m/K | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 150 to 200 | °C | |
| Barrel 2 zone temperature | 150 to 200 | °C | |
| Barrel 3 zone temperature | 150 to 200 | °C | |
| Barrel 4 zone temperature | 150 to 200 | °C | |
| Barrel 5 zone temperature | 150 to 200 | °C | |
| Head temperature | 200 | °C | |
| Nozzle temperature | 210 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |