| About |
|---|
| Polidiemme® XLPO-可交联聚烯烃 弹性体类化合物c可通过环境湿度进行交联，含有与催化剂母料一起使用的硅烷预接枝基体化合物（ SIOPLAS ®方法）。 满足以下标准： – Cenelec HD 22.1 EI4， EI6， EI7 和EM3； EN 50363-0 G8；IEC 60502 EPR； IEC 60092/351 EPR； BS 7655 RS5 和GP7；VDE 0207/20 3GI3&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | XLPO |
| Material Status | Commercial: Active |
| Features | Good flexibility,Crosslinked,Low toxicity |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.880 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.80 | g/10min | Internal Method |
| Water absorption rate | |||
| 100℃，24hr | 1.00 | mg/cm² | IEC 60811 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 3.50 | kN/m | ASTM D1938 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Changes in mechanical properties after air bomb aging test at 0.5MPa, 127 ℃, 40 hr | IEC 60811 | ||
| Change in tensile elongation | -9 | % | IEC 60811 |
| Changes in mechanical properties after hot air aging test at 100 ℃ for 336 hours | IEC 60811 | ||
| The rate of change in tensile strength | 10 | % | IEC 60811 |
| Change in tensile elongation | 0 | % | IEC 60811 |
| Changes in mechanical properties after hot air aging test, 135 ℃, 168 hr | IEC 60811 | ||
| The rate of change in tensile strength | 18 | % | IEC 60811 |
| Change in tensile elongation | 14 | % | IEC 60811 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| thermosetting | IEC 60811 | ||
| Maximum permanent elongation after cooling: 200 ℃ | 0.0 | % | IEC 60811 |
| Elongation at break under load: 200 ℃ | 50 | % | IEC 60811 |
| Maximum permanent elongation after cooling: 250 ℃ | 0.0 | % | IEC 60811 |
| Elongation at break under load: 250 ℃ | 70 | % | IEC 60811 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | IEC 60502 | ||
| 20 ℃ | 4.1E+15 | ohms·cm | IEC 60502 |
| 90 ℃ | 1.4E+14 | ohms·cm | IEC 60502 |
| Dielectric strength | 32 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 kHz | 2.30 | ASTM D150 | |
| Dissipation factor | |||
| 1 kHz | 1.0E-3 | ASTM D150 | |
| Insulation resistance constant | IEC 60502 | ||
| 20℃ | 15000 | Mohms·km | IEC 60502 |
| 90℃ | 500 | Mohms·km | IEC 60502 |
| Chemical properties | Nominal value | Unit | Test method |
|---|---|---|---|
| IRM 902 Oil Immersion Test, 23 ℃, 24 hr | IEC 60811 | ||
| The rate of change in tensile strength | -11 | % | IEC 60811 |
| Change in tensile elongation | -8 | % | IEC 60811 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 18 | ISO 868 | |
| tensile strength | |||
| fracture | 10.0 | MPa | IEC 60811 |
| Tensile strain | |||
| fracture | 500 | % | IEC 60811 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 120 to 140 | °C | |
| Barrel 2 zone temperature | 120 to 150 | °C | |
| Barrel 3 zone temperature | 130 to 160 | °C | |
| Barrel 4 zone temperature | 140 to 170 | °C | |
| Ring temperature | 140 to 170 | °C | |
| Head temperature | 140 to 170 | °C | |
| Nozzle temperature | 140 to 170 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |