Polifil® PC GFPC-40

About
Polifil ® GFPC series compounds offer a combination of improved dimensional stability and decreased flammability. The excellent balance of physical properties make the Polifil ® glass-filled polycarbonate line an excellent choice for electrical, appliance and hardware applications. Standard processing techniques are applicable. Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations for your application.&&

About

Polifil ® GFPC series compounds offer a combination of improved dimensional stability and decreased flammability. The excellent balance of physical properties make the Polifil ® glass-filled polycarbonate line an excellent choice for electrical, appliance and hardware applications. Standard processing techniques are applicable. Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations for your application.&&

Product Description
Generic	Polycarbonate
Material Status	Commercial: Active
Features	Good Dimensional Stability,Flame Characteristics
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.52	g/cm³	ASTM D792
Melt Flow Rate
300℃，1.20kg	5.0	g/10min	ASTM D1238
Shrinkage rate
MD：3.2 mm	0.20	%	ASTM D955
Water absorption rate
24hr	0.15	%	ASTM D570

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	96	J/m	ASTM D256
Drop hammer impact
23℃，12.7 mm	0.452	J	ASTM D3029

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature			ASTM D648
0.45 MPa, unannealed	149	℃	ASTM D648
1.8 MPa, unannealed	146	℃	ASTM D648

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	120		ASTM D785
Tensile modulus
23℃	11000	MPa	ASTM D638
tensile strength
23℃	138	MPa	ASTM D638
Tensile strain			ASTM D638
Yield, 23 ℃	2.0	%	ASTM D638
Fracture, 23 ℃	3.0	%	ASTM D638
Bending modulus
Tangent, 23 ℃	9310	MPa	ASTM D790
bending strength
23℃	185	MPa	ASTM D790

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	121	°C
Drying time	4.0 to 5.0	hr
Barrel rear temperature	266 to 277	°C
Barrel middle temperature	271 to 282	°C
Barrel front temperature	277 to 293	°C
Nozzle temperature	282 to 299	°C
Processing (melt) temperature	277 to 304	°C
Mold temperature	77 to 99	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.