Polifil® PP C-10

About
Polifil ® C series compounds are homopolymer polypropylene resins reinforced with fine particle size calcium carbonate. They combine high impact with stiffness, good colorability, resistance to environmental stress-cracking, good surface, and low mold shrinkage. Polifil ® C products in the 20 to 40% range are UL94 HB rated. These compounds are used in appliances, electrical components, housewares, toys, automotive, and utility products. Standard processing techniques are applicable. Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations for your application.&&

About

Polifil ® C series compounds are homopolymer polypropylene resins reinforced with fine particle size calcium carbonate. They combine high impact with stiffness, good colorability, resistance to environmental stress-cracking, good surface, and low mold shrinkage. Polifil ® C products in the 20 to 40% range are UL94 HB rated. These compounds are used in appliances, electrical components, housewares, toys, automotive, and utility products. Standard processing techniques are applicable. Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations for your application.&&

Product Description
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Good Rigidity,Good heat aging resistance,Good surface appearance,Low contractility,High ESCR,Homopolymer,Good coloring
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.978	g/cm³	ASTM D792
Melt Flow Rate
230℃，2.16kg	8.0 to 12	g/10min	ASTM D1238
Shrinkage rate
MD：3.2 mm	1.5	%	ASTM D955

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	37	J/m	ASTM D256
Drop hammer impact
23℃，12.7 mm	2.71	J	ASTM D3029

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature			ASTM D648
0.45 MPa, unannealed	93.3	℃	ASTM D648
1.8 MPa, unannealed	54.4	℃	ASTM D648

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	72		ASTM D1415
Tensile modulus
23℃	1450	MPa	ASTM D638
tensile strength
23℃	30.3	MPa	ASTM D638
Tensile strain			ASTM D638
Yield, 23 ℃	8.0	%	ASTM D638
Fracture, 23 ℃	30	%	ASTM D638
Bending modulus
Tangent, 23 ℃	1590	MPa	ASTM D790
bending strength
23℃	35.2	MPa	ASTM D790

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	82 to 104	°C
Drying time	1.0 to 2.0	hr
Barrel rear temperature	199 to 210	°C
Barrel middle temperature	210 to 221	°C
Barrel front temperature	221 to 232	°C
Nozzle temperature	227 to 232	°C
Processing (melt) temperature	204 to 260	°C
Mold temperature	10 to 27	°C
Injection speed	快速
Back pressure	0.345 to 0.689	MPa
Screw speed	50 to 100	rpm

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.