| Polimid A 35 GF V0F K is a Polyamide 66 (Nylon 66) material filled with 35% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or Latin America. Important attributes of Polimid A 35 GF V0F K are: Flame Rated Flame Retardant&& |
| Product Description | |
|---|---|
| Supplier | Poliblend |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Electrical Properties,Self-extinguishing,V-0 |
| Availabilitys | Africa & Middle East ,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.44 | g/cm³ | ISO 1183 |
| Shrinkage rate | 0.30 to 0.60 | % | |
| Water absorption rate | |||
| 23℃，24hr | 0.50 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 9500 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| yield | 150 | MPa | ISO 527-2 |
| fracture | 150 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| yield | 2.0 | % | ISO 527-2 |
| fracture | 2.0 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 11 | kJ/m² | ISO 180/A |
| Notched impact strength of cantilever beam | 95 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 260 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 248 | ℃ | ISO 75-2/A |
| Continuous use temperature | 125 | ℃ | |
| Vicat Softening Temp | 255 | ℃ | ISO 306/A120 |
| Ball pressure test | |||
| 165℃ | 通过 | IEC 60695-10-2 | |
| Melting temperature | 260 | ℃ | DSC |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | 525 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.80 mm | V-0 | UL 94 | |
| 1.60 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 2.0 mm | 950 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 2 mm | 775 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 100 | °C | |
| Drying time | > 3.0 | hr | |
| Processing (melt) temperature | 270 to 290 | °C | |
| Mold temperature | 80 to 90 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Without Load |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |