| About |
|---|
| PolyAxis LP-8000 is a high density polyethylene intended for the rotational molding industry. This stiff yet tough compound has been used in watercraft with good success.&& |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | mHDPE |
| Material Status | Commercial: Active |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.945 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 3.6 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, roll forming | 22.1 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, roll forming | 500 | % | ASTM D638 |
| Bending modulus | |||
| 1% cut, roll forming | 1000 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod notched impact strength | |||
| -40 ℃, 3.2mm, roll forming | 88 | J | ARM |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Compression Molded |
| 3. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |