| APPLICATIONS : Fibre spinning (short quench), Resistance to gas fading.&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Negative |
| Features | Solvent resistance,Homopolymer |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 9.0 to 13 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 35.5 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 10 | % | ASTM D638 |
| Bending modulus | |||
| 1% secant | < 1500 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 35 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 107 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 55.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| — | 155 | ℃ | ASTM D1525 4 |
| — | 96.0 | ℃ | ASTM D1525 5 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Yellowness index | < 0.0 | YI | DIN 6167 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.051 in/min |
| 4. Rate A (50°C/h), Loading 1 (10 N) |
| 5. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |