| About |
|---|
| POLYCOMPO PE 3520L is a Linear Low Density Polyethylene product. It can be processed by blown film or cast film and is available in Asia Pacific. Typical application: Film. Characteristics include: Good Sealability Heat Resistant Rigid&& |
| Product Description | |
|---|---|
| Supplier | POLYCOMPO |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good heat sealing,High Heat Resistance |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.931 | g/cm³ | ISO 1183 |
| Melt Flow Rate | 2.1 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| injection molding | 1000 | hr | ASTM D1693 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 无断裂 | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 115 | ℃ | ASTM D1525 , ISO 306 |
| Crystallization peak temperature | |||
| DSC | 124 | ℃ | ASTM D3418 , ISO 3146 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, injection molding | 62 | ASTM D2240 , ISO 868 | |
| tensile strength | ISO 527-2 | ||
| Yield, injection molding | 14.0 | MPa | ISO 527-2 |
| Fracture, injection molding | 26.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, injection molding | 500 | % | ISO 527-2 |
| Bending modulus | |||
| injection molding | 420 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |