POLYFLAM® HSF 36

About
High impact flame-retardant PS grade; without PBDE&&

Product Description
Supplier	A. Schulman
Generic	PS (GPPS)
Material Status	Commercial: Active
Features	Flame Characteristics,V-0,5VA,5VB
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.18	g/cm³	ISO 1183/A
Melt Volume Rate
200℃，5 kg	5.00	cm³/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	2100	MPa	ISO 527-2/1A/1
tensile strength
yield	30.0	MPa	ISO 527-2/1A/50
Tensile strain
yield	2.0	%	ISO 527-2/1A/50

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179/1eA
-30℃	2.0	kJ/m²	ISO 179/1eA
23℃	10	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength			ISO 179/1eU
-30℃	40	kJ/m²	ISO 179/1eU
23℃	70	kJ/m²	ISO 179/1eU

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	75.0	℃	ISO 75-2/Af
0.45 MPa, unannealed	86.0	℃	ISO 75-2/Bf
Vicat Softening Temp
A50	100	℃	ISO 306/A50
B50	86.0	℃	ISO 306
Ball pressure test
80℃	Pass		IEC 60695-10-2
1.5 mm	50.0	℃	UL 746
3.0 mm	50.0	℃	UL 746
Relative temperature index
Electrical performance			UL 746
Strength mechanical performance			UL 746
Impact mechanical performance			UL 746
1.5 mm	50.0	℃	UL 746
3.0 mm	50.0	℃	UL 746
1.5 mm	50.0	℃	UL 746
3.0 mm	50.0	℃	UL 746

Electrical performance	Nominal value	Unit	Test method
Compared to the leakage tracing index	350	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Burning rate			ISO 3795
1.5mm, automatic fire extinguishing	0.0	mm/min	ISO 3795
3.0 mm, automatic fire extinguishing	0.0	mm/min	ISO 3795
Flame retardant level			UL 94
1.50 mm	V-0		UL 94
3.00 mm	V-0 5VA		UL 94
2.00 mm	5VB		UL 94
4.00 mm	5VA		UL 94
Flammability level			IEC 60695-11-10, -20
1.5 mm	V-0		IEC 60695-11-10, -20
3.0 mm	V-0 5VA		IEC 60695-11-10, -20
4.0 mm	5VA		IEC 60695-11-10, -20
2.0 mm	5VB		IEC 60695-11-10, -20
Glowing wire flammability index			IEC 60695-2-12
1.5 mm	960	℃	IEC 60695-2-12
3.0 mm	960	℃	IEC 60695-2-12
Igniting temperature of the hot wire			IEC 60695-2-13
1.5 mm	625	℃	IEC 60695-2-13
3 mm	625	℃	IEC 60695-2-13
Extreme oxygen index	26	%	ISO 4589-2

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	70 to 80	°C
Drying time	2.0 to 4.0	hr
Barrel rear temperature	190	°C
Barrel middle temperature	200	°C
Barrel front temperature	210	°C
Nozzle temperature	220	°C
Processing (melt) temperature	190 to 220	°C
Mold temperature	30 to 60	°C
Injection pressure	80.0 to 120	MPa
Injection speed	Slow-Moderate
Hold pressure	40.0 to 90.0	MPa
Back pressure	5.00 to 10.0	MPa
Cushion	< 5.00	mm
Screw speed	< 300	mm/sec

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.