POLYFLAM® RABS 90000 UV5

About
POLYFLAM® RABS 90000 UV5 Flame retardant ABS standard grade without PBDE and higher thermal stability&&POLYFLAM® RABS 90000 UV5 ABS Flame Retardant&&

Product Description
Supplier	A. Schulman
Generic	ABS
Material Status	Commercial: Active
Features	Weather resistance is good,Excellent Processability,Low to No Fogging,Flame Characteristics,Heat Stabilized,V-0,5VA
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.20	g/cm³	ISO 1183/A
Melt Volume Rate
220℃，10 kg	30.0	cm³/10min	ISO 1133

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179/1eA
-30℃	5.0	kJ/m²	ISO 179/1eA
23℃	10	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength			ISO 179/1eU
-30℃	45	kJ/m²	ISO 179/1eU
23℃	80	kJ/m²	ISO 179/1eU

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	80.0	℃	ISO 75-2/Af
0.45 MPa, unannealed	92.0	℃	ISO 75-2/Bf
Vicat Softening Temp
A50	105	℃	ISO 306/A50
B50	96.0	℃	ISO 306
Ball pressure test
90℃	Pass		IEC 60695-10-2
Relative temperature index
Electrical performance			UL 746
Strength mechanical performance			UL 746
Impact mechanical performance			UL 746
1.5 mm	60.0	℃	UL 746
3.0 mm	60.0	℃	UL 746

Electrical performance	Nominal value	Unit	Test method
Compared to the leakage tracing index	475	V	IEC 60112
High Arc Burning Index (HAI)			UL 746
1.5 mm	PLC 3		UL 746
3.0 mm	PLC 3		UL 746
Hot wire ignition
HWI			UL 746
3.0 mm	PLC 0		UL 746

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Burning rate
3.0 mm, automatic fire extinguishing	0.0	mm/min	ISO 3795
Flame retardant level			UL 94
1.50 mm	V-0		UL 94
3.00 mm	V-0		UL 94
Flammability level			IEC 60695-11-10, -20
0.8 mm	V-0		IEC 60695-11-10, -20
1.5 mm	V-0		IEC 60695-11-10, -20
3.0 mm	V-0		IEC 60695-11-10, -20
4.0 mm	5VA		IEC 60695-11-10, -20
Glowing wire flammability index			IEC 60695-2-12
1.5 mm	960	℃	IEC 60695-2-12
3.0 mm	960	℃	IEC 60695-2-12
Igniting temperature of the hot wire			IEC 60695-2-13
1.5 mm	725	℃	IEC 60695-2-13
3 mm	725	℃	IEC 60695-2-13
Extreme oxygen index	28	%	ISO 4589-2

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	2200	MPa	ISO 527-2/1A/1
tensile strength
yield	42.0	MPa	ISO 527-2/1A/50
Tensile strain
yield	3.0	%	ISO 527-2/1A/50
Ball hardness	113	MPa	ISO 2039-1

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	70 to 80	°C
Drying time	2.0 to 4.0	hr
Barrel rear temperature	220	°C
Barrel middle temperature	230	°C
Barrel front temperature	240	°C
Nozzle temperature	240	°C
Processing (melt) temperature	220 to 240	°C
Mold temperature	40 to 60	°C
Injection pressure	80.0 to 120	MPa
Injection speed	Slow-Moderate
Hold pressure	40.0 to 90.0	MPa
Back pressure	5.00 to 10.0	MPa
Cushion	< 5.00	mm
Screw speed	< 300	mm/sec

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.